Artificial Graphite HC15 for Power Lithium Battery
Category:
Artificial graphite
Advantages:
High energy density
Long battery life
1.5C charging rate
Application:
Artificial Graphite HC15 is widely used to Power Lithium batteries. Power lithium battery has the advantages of high energy, high battery voltage, wide operating temperature range, long storage life and so on. It has been widely used in military and civil small electrical vehicle (EV) batteries or large capacity and power batteries in other applicaitosn, partly replacing the traditional battery.
Tips:
The material design first discharge capacity is recommended to be 350mAh/g, and the tap density is recommended to be controlled in 1.60g/cc and below. This product is suitable for aqueous solution lithium battery system.
Packaging requirements:
HC15 artificial graphite shall be packed into a plastic bag with a specification of 650mm×950mm, sealed and then placed into a carton with a weight of 25+0.02kg/ box, or according to customer requirements packaging.
Transportation and storage:
a. The product should be stored in a place where dry, ventilated and no other pollution sources (recommended: temperature ≤ 45 ° C, humidity ≤85%);
b. Product stacking should be neat, clean, production lot number, production date, etc. should be clearly identified;
c. During the transportation process, it should be gently put, so as not to damage the packaging; Any products leaking out of the bag shall not be returned to the box.
d. The shelf life is 2 years in a normal temperature state.
Packaging and product identification:
H5 product packaging must be marked with the following information:
A) Product Name
B) Batch Number of product
C) Product weight
D) Date
E) Company Name
Matters needing attention:
A) Ensure that the capacity of the negative electrode per unit area is greater than or equal to that of the positive electrode per unit area to avoid lithium evolution during charging.
B) Ensure that there is a good interface between the isolation film and the electrode.
C) The surface density and compaction density of the electrode will affect the performance of the rate capacity and performance.
D) The product is of secondary particle + single particle structure, and it is recommended that the design pressure below 1.55-1.60g/cc is the best.
Technical indicators:
Number | Name | Unit | Standard | Typical values | |
1 |
Particle size | Dmin | um | ≥1.5 | 1.78 |
D10 | um | 6.0±2.0 | 6.34 | ||
D50 | um | 14.0±2.0 | 13.97 | ||
D90 | um | 24.0±3.0 | 24.54 | ||
Dmax | um | ≤55 | 45.19 | ||
2 | TAP | g/cc | 1.0±0.1 | 1.03 | |
3 | SSA | m2/g | 1.0-2.0 | 1.50 | |
4 | C | % | ≥99.95 | 99.985 | |
5 | Tap Density | g/cc | 1.60-1.63 | ~1.60 | |
First discharge capacity | mAh/g | ≥352 | 354.4 | ||
6 | True Density | g/cc | ≥2.20 | 2.27 | |
7 | First discharge capacity | % | ≥92% | 95.4 | |
8 |
Trace elements | Fe | ppm | ≤15 | 7.98 |
Co | ppm | ≤5 | 0.34 | ||
Cu | ppm | ≤5 | -- | ||
Ni | ppm | ≤5 | 0.12 | ||
Al | ppm | ≤5 | -- |
Particle Size Distribution:
Discharge Capacity:
XRD:
Artificial Graphite YXA-H for Energy Storage Battery materials meet all power specifications including high capacity (about 346.8mAh/g) and high first cycle efficiency (about 95.9%). If you have a dem
The powder graphite TOB high purity natural graphite powder for lithium battery anode raw material parameters refer to the specific properties of the powdered graphite that can be used as an anode mat
The parameters used to sinter graphite in a sagger for cemented carbide Li-Battery anode powder typically include:
The high energy density artificial graphite powder (AGP) used in lithium-ion batteries is an important factor affecting the performance of the battery. The specific parameters of AGP can vary dependin
The parameters you mentioned, such as high rate factory outlet artificial graphite powder of anode material for Li-ion battery, refer to the composition and properties of the material used in lithium-
Conductive graphite powder is a useful component in lithium-ion batteries, particularly in the anode and cathode regions of the battery.
The parameter "MCMB Graphite Powder for Li-ion Battery Anode Raw Materials" refers to the raw material for lithium-ion battery anodes, specifically for the material known as Magnesium Carbonate (MCMB)
The parameters you provided refer to the chemical properties of an artificial graphite powder used in lithium-ion batteries. Here are some common parameters:
The micro-grain graphite raw material powder can be used as an electrode material in lithium battery production, particularly for the application of lithium-ion batteries. The parameter parameters tha
The given specifications seem to refer to various types of graphite powder and battery elements.
The particle size of the bettery graphite powder used as an anode material in batteries can vary depending on the manufacturer and application requirements. However, typically it is expected that the
The specific parameters for supply graphite powder for Li-ion battery anodes will depend on the application and requirements of the battery. However, some common parameters that may be important to co
Conductive graphite powder is used as an anode material in lithium battery cells because it has high surface area and excellent electrical conductivity, which allows it to transport ions quickly durin
The "Industrial Grade Graphite Powder Fire Proof Material Flake Graphite Powder" product is an industrial-grade flake graphite powder, which is used as the raw material in lithium-ion battery producti
New Li-On Material Lithium Ion Battery Anode Materials Low硫 Graphite with High Quality Parameters:
Artificial Graphite Powder (AGP) is an effective anode material for lithium-ion batteries due to its high energy density, high rate capability, and low dendrite formation. The parameter for AGP in a l
Artificial Graphite Powder Lithium ion Battery Anode Materials typically consist of various components, such as:
Artificial graphite powder is often used as the electrode material in lithium-ion batteries, and it has many advantages over traditional electrode materials like carbon.
Artificial Graphite Anode Material Powder Synthetic Graphite Production For Li-ion Battery Anode Material Parameter:
Factory Direct Source Spherical graphite powder is a high-quality spherical graphite powder that can be used as an electrode material in lithium-ion batteries. The specific parameter of the lithium ba
The quality of high purity modified artificial graphite electrode powder lithium-ion battery anode material depends on various factors, including the method used for production, processing conditions,
Artificial Graphite YXA-H2 for Energy Storage Battery materials meet all power specifications including high capacity (about 346.3mAh/g) and high first cycle efficiency (about 95.9%). If you have a de
Artificial Graphite H9 for Power Lithium Battery materials meet all power specifications including high capacity (about 354.9mAh/g) and high first cycle efficiency (about 95.3%). If you have a demand
Artificial Graphite HC15 for Power Lithium Battery materials meet all Power specifications including high capacity (about 354.4mAh/g) and high first cycle efficiency (about 95.4%). If you have a deman
GS-16 Modified artificial graphite meet all power specifications including high capacity (about 346.8mAh/g) and high first cycle efficiency (about 95.9%). If you have a demand for GS-16 Modified artif
SYC-1 Silicon-Carbon Anode Materials, Lithium Graphite Battery meet all power specifications including high capacity (about 346.8mAh/g) and high first cycle efficiency (about 95.9%). If you have a dem
Anthracite artificial graphite, Graphite Particle Size meet all power specifications including high capacity (about 346.8mAh/g) and high first cycle efficiency (about 95.9%). If you have a demand for
Anthracite Artificial Graphite Powder meet all power specifications including high capacity (about 346.8mAh/g) and high first cycle efficiency (about 95.9%). If you have a demand for Particle Size 681
Artificial compound graphite meet all power specifications including high capacity (about 346.8mAh/g) and high first cycle efficiency (about 95.9%). If you have a demand for artificial compound graphi
Prepare edits:Silica can be obtained by the rapid oxidation of silicon dioxide with elemental silica at high temperature: SiO2 + Si → 2SiO Use edits:Solid silicon monoxide can be used as insulating ma
In the Si/C composite system, Si particles serve as the active material to provide lithium storage capacity. C can not only buffer the volume change of the silicon anode during the discharge process,
Natural Graphite 216-3 for 18650 Lithium-ion Battery Anode materials meet all required specifications including high capacity (>358 mAh/g) and high first cycle efficiency (95%). If you have a demand f
Artificial Graphite GS16-Q for Digital Products Large Capacity Lithium-ion Battery materials meet all digital products specifications including high capacity (about 359.3 mAh/g) and high first cycle e
Artificial Graphite H5 for Power Tool Lithium Battery materials meet all Power Tool specifications including high capacity (about 354.4 mAh/g) and high first cycle efficiency (about 95.4%). If you hav
Artificial Graphite GS16-S for Digital Products Large Capacity Lithium-ion Battery materials meet all digital products specifications including high capacity (about 357 mAh/g) and high first cycle eff
Copyright © 2024 By Graphite-Corp